CESSNA 172A near Payson, AZ — 2009-10-03

Final reportWPR10LA004
Sign in to save
Date
2009-10-03
Location
Payson, AZ, USA
Airport
PAN
Aircraft
CESSNA 172A
Registration
N7810T
Category
Airplane
Highest injury
None
Fatalities
0

Probable cause

The stress corrosion cracking of the nose gear landing fork, which resulted in the fork's failure during landing.

NTSB narrative

The pilot reported that, as the airplane touched down, the nose gear separated and the airplane veered to the left before coming to rest on the runway. During the event the right wing was substantially damaged. Postaccident examination of the separated nose landing gear fork indicated that the alloy used for forging the part was 2014 series aluminum, which is susceptible to stress corrosion cracking (SCC) given the proper environment and a continuous stress state. A Safety Board metallurgist concluded that the fracture characteristics were consistent with SCC, with slow crack growth over time. The crack appeared to have originated from a point on the surface of the bolt hole bore and propagated upwards and outwards. The last annual inspection of the airplane was conducted about two weeks prior to the accident, although the investigation was unable to determine if the crack would have been visible to the unaided eye during a routine inspection.

NTSB coding

Evidence available

  • Photos
  • 5 docket documents
View NTSB final reportView NTSB docket

Docket documents5

Related mishaps